Lubricated SC631 NC010, China Lubricated SC631 NC010 Manufacturers, Suppliers, Factory - SHANGHAI QISHEN PLASTIC INDUSTRY CO., LTD

Parameter

Material Technical Datasheet
SC631 NC010
FEATURES		APPLICATIONS
Lubricated		Medical healthcare application
Low friction
Nucleated
Properties	Test Standard	Test Condition	Units	Typical Values
Physical Properties
Density	ISO 1183		kg/m³	1420
Shrinkage Flow	ISO 294		%	1.9
Shrinkage xFlow	ISO 294		%	1.8
Water Absorption	ISO 62	2.00mm	%	0.9
Water Absorption	ISO 62	24hr In Water	%	0.2
Melt Index	ISO 1133	190℃2.16kg	cm³/10min	6
Melt Index	ISO 1133	190℃2.16kg	g/10min	7
		Hardness
Rockwell Hardness M(Scale)	ISO 2039			*
Rockwell Hardness R(Scale)	ISO 2039			*
Mechanical Properties
Tensile Modulus	ISO 527		Mpa	3300
Tensile Strength	ISO 527		Mpa	74
Elongation Yield	ISO 527		%	15
Elongation Break	ISO 527		%	35
Poisson Ratio	INTERNAL METHOD			0.37
Tensile Creep Modulus	ISO 899	1hr	Mpa	*
Tensile Creep Modulus	ISO 899	1000hr	Mpa	*
Flexural Strength	ISO 178	3.5%Strain	Mpa	86
Flexural Modulus	ISO 178		Mpa	3100
lzod Notch lmpact	ISO 180	23'℃Type A	kJ/㎡	10
Izod Notch lmpact	ISO 180	-40°CType A	kJ/㎡	8
Charpy Notch lmpact	ISO 179	23°C1eA	kJ/㎡	9
Charpy Notch lmpact	ISO 179	-30°C1eA	kJ/㎡	8
Charpy Un-notch lmpact	ISO 179	23°C	kJ/㎡	300
CharpyUn-notch lmpact	ISO 179	-30°C	kJ/㎡	250
Thermal Properties
Thermal Properties	Test Standard	Test Condition	Units	Data
HDT 1.8MPa	ISO 75	1.8MPa 6.4mm	℃	103
HDT 0.45MPa	ISO 75		℃	165
Vicat softeningTemperature	ISO 306	50°C/hr 50N	℃	160
Melting Temperature	ISO 11357	10°C/min	℃	178
CLE FIow	ISO 11359		m/m/K	1.10E-04
CLE xFlow	ISO 11359		m/m/K	1.10E-04
Electrical Performance
Dielectric Strength	ASTM D149	1.00E+13	KV/MM
Surface Resistivity	IEC 62631-3-2	1.00E+15	Ω
Dielectric Constant 100Hz	IEC 62631-2-1	3.8
Dielectric Constant 1Hz	IEC 62631-2-1	3.8
Dissipation Factor 100MHz	IEC 62631-2-1	*
Dissipation Factor 1MHz	IEC 62631-2-1	0.005
Flame Retardancy
Flame Retardancy	Test Standard	Data
Flame Rating All Color 0.75mm	UL94	*
Flame Rating All Color 1.5mm	UL94	*
Flame Rating All Color 3.0mm	UL94	*
Buming Rate	ISO 3795	*	mm/min
VDA Properties
Emission	VDA 275	8	MG/KG
Emission of organic compounds	VDA 275	*	μm/g
Fogging F-value Condenate	ISO 6452	*	%
Fogging G-value Condenate	ISO 6452	*	mg
UL
Flame Retardancy	Test Standard	Data	Units
UL FlameRating ALL 0.75mm	UL94	*
HWI ALL0.75mm	UL 746A	*	PLC
HWI ALL0.75mm	UL 746A	*	PLC
RTI Elec ALL0.75mm	UL746B	*	℃
RTI lmp ALL 0.75mm	UL746B	*	℃
RTI Str ALL 0.75mm	UL746B	*	℃
UL FlameRating ALL 1.5mm	UL94	*
HWI ALL1.5mm	UL 746A	*	PLC
HWI ALL1.5mm	UL 746A	*	PLC
RTI Elec ALL1.5mm	UL746B	*	℃
RTI lmp ALL 1.5mm	UL746B	*	℃
RTI Str ALL 1.5mm	UL746B	*	℃
UL FlameRating ALL 3.0mm	UL94	*
HWI ALL3.0mm	UL 746A	*	PLC
HWI ALL3.0mm	UL 746A	*	PLC
RTI Elec ALL3.0mm	UL746B	*	℃
RTI lmp ALL 3.0mm	UL746B	*	℃
RTI Str ALL 3.0mm	UL746B	*	℃
UL FlameRating ALL6.0mm	UL94	*
HWI ALL6.0mm	UL 746A	*	PLC
HWI ALL6.0mm	UL 746A	*	PLC
RTI Elec ALL6.0mm	UL746B	*	℃
RTI lmp ALL 6.0mm	UL746B	*	℃
RTI Str ALL 6.0mm	UL746B	*	℃
CTI	IEC 60112	*	PLC
HVTR	UL 746A	*	PLC
Arc resistance	ASTM D495	*	PLC
Injection Molding
Injection Molding			Units	Data
Drying Temperature			℃	80
Drying Time			hr	2～4
Water Content Control			%	≤0.2
Melt Temperature Optimum			℃	215
Min. Melt Temperature			℃	210
Max. Melt Temperature			℃	220
Mould Temperature			℃	90
Min. Mould Temperature			℃	80
Max. Mould Temperature			℃	100
Holding Pressure			MPa	80～100
Hold Pressure Time			s/mm	7.54
Annealing Time			min/mm	30
Annealing Temperature			℃	160
Extrusion molding
Dry Temperature			℃	75~85
Dry Time			hr	2~4
Water Content Control			%	≤0.2
Melt Temperature			℃	195~205
Melt Temperature Optimum			℃	200

All Categories

Lubricated SC631 NC010