Home > Product > Raw Material > POM
| Material Technical Datasheet | ||||
| 900P BK602 | ||||
| FEATURES | APPLICATIONS | |||
| Lubricated | ||||
| Low friction | ||||
| Good moldability | ||||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Density | ISO 1183 | kg/m³ | 1420 | |
| Shrinkage Flow | ISO 294 | % | 1.8 | |
| Shrinkage xFlow | ISO 294 | % | 1.7 | |
| Water Absorption | ISO 62 | 2.00mm | % | 0.4 |
| Water Absorption | ISO 62 | 24hr In Water | % | * |
| Melt Index | ISO 1133 | 190℃2.16kg | cm³/10min | * |
| Melt Index | ISO 1133 | 190℃2.16kg | g/10min | 25 |
| Hardness | ||||
| Rockwell Hardness M(Scale) | ISO 2039 | * | ||
| Rockwell Hardness R(Scale) | ISO 2039 | * | ||
| Mechanical Properties | ||||
| Tensile Modulus | ISO 527 | Mpa | 3300 | |
| Tensile Strength | ISO 527 | Mpa | 70 | |
| Elongation Yield | ISO 527 | % | 12 | |
| Elongation Break | ISO 527 | % | 17 | |
| Poisson Ratio | INTERNAL METHOD | 0.37 | ||
| Tensile Creep Modulus | ISO 899 | 1hr | Mpa | * |
| Tensile Creep Modulus | ISO 899 | 1000hr | Mpa | * |
| Flexural Strength | ISO 178 | 3.5%Strain | Mpa | * |
| Flexural Modulus | ISO 178 | Mpa | 3000 | |
| lzod Notch lmpact | ISO 180 | 23'℃Type A | kJ/㎡ | 7 |
| Izod Notch lmpact | ISO 180 | -40°CType A | kJ/㎡ | 7 |
| lzod un-Notch lmpact | ISO 180 | 23'℃Type A | kJ/㎡ | * |
| Izod un-Notch lmpact | ISO 180 | -40°CType A | kJ/㎡ | * |
| Charpy Notch lmpact | ISO 179 | 23°C1eA | kJ/㎡ | 7 |
| Charpy Notch lmpact | ISO 179 | -30°C1eA | kJ/㎡ | 6 |
| Charpy Un-notch lmpact | ISO 179 | 23°C | kJ/㎡ | 130 |
| CharpyUn-notch lmpact | ISO 179 | -30°C | kJ/㎡ | * |
| Friction Coefficient Dynamic VS | ASTM D1894 | 1HR | * | |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| HDT 1.8MPa | ISO 75 | 1.8MPa 6.4mm | ℃ | 98 |
| HDT 0.45MPa | ISO 75 | ℃ | 161 | |
| Vicat softeningTemperature | ISO 306 | 50°C/hr 50N | ℃ | * |
| Melting Temperature | ISO 11357 | 10°C/min | ℃ | 178 |
| CLE FIow | ISO 11359 | m/m/K | 1.00E-04 | |
| CLE xFlow | ISO 11359 | m/m/K | 1.00E-04 | |
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Flame Rating BK 1.5mm | UL94 | HB | ||
| Flame Rating BK 3.0mm | UL94 | HB | ||
| Flame Rating BK 6.0mm | UL94 | HB | ||
| Buming Rate 1.00mm | ISO 3795 | 23 | MM/MIN | |
| Electrical Performance | ||||
| Electrical Performance | Test Standard | Data | Units | |
| Volume Resistivity | IEC 62631 | * | Ω.m | |
| Surface Resistivity | IEC 62631-3-2 | * | Ω | |
| Dielectric Constant 100Hz | IEC 62631-2-1 | * | ||
| Dielectric Constant 1Hz | IEC 62631-2-1 | * | ||
| Dissipation Factor 100MHz | IEC 62631-2-1 | * | ||
| Dissipation Factor 1MHz | IEC 62631-2-1 | * | ||
| CTl | 60112 | * | V | |
| VDA Properties | ||||
| Emission | VDA 275 | * | MG/KG | |
| Emission of organic compounds | VDA 275 | * | μm/g | |
| Fogging F-value Condenate | ISO 6452 | * | % | |
| Fogging G-value Condenate | ISO 6452 | * | mg | |
| UL | ||||
| Flame Retardancy | Test Standard | Data | Units | |
| UL FlameRating ALL 0.75mm | UL94 | HB | ||
| HWI ALL0.75mm | UL 746A | 4 | PLC | |
| HWI ALL0.75mm | UL 746A | 0 | PLC | |
| RTI Elec ALL0.75mm | UL746B | 50 | ℃ | |
| RTI lmp ALL 0.75mm | UL746B | 50 | ℃ | |
| RTI Str ALL 0.75mm | UL746B | 50 | ℃ | |
| UL FlameRating ALL 1.5mm | UL94 | HB | ||
| HWI ALL1.5mm | UL 746A | 4 | PLC | |
| HWI ALL1.5mm | UL 746A | 0 | PLC | |
| RTI Elec ALL1.5mm | UL746B | 110 | ℃ | |
| RTI lmp ALL 1.5mm | UL746B | 85 | ℃ | |
| RTI Str ALL 1.5mm | UL746B | 90 | ℃ | |
| UL FlameRating ALL 3.0mm | UL94 | HB | ||
| HWI ALL3.0mm | UL 746A | 3 | PLC | |
| HWI ALL3.0mm | UL 746A | 0 | PLC | |
| RTI Elec ALL3.0mm | UL746B | 110 | ℃ | |
| RTI lmp ALL 3.0mm | UL746B | 90 | ℃ | |
| RTI Str ALL 3.0mm | UL746B | 95 | ℃ | |
| UL FlameRating ALL6.0mm | UL94 | * | ||
| HWI ALL6.0mm | UL 746A | * | PLC | |
| HWI ALL6.0mm | UL 746A | * | PLC | |
| RTI Elec ALL6.0mm | UL746B | * | ℃ | |
| RTI lmp ALL 6.0mm | UL746B | * | ℃ | |
| RTI Str ALL 6.0mm | UL746B | * | ℃ | |
| CTI | IEC 60112 | 0 | PLC | |
| HVTR | UL 746A | 0 | PLC | |
| Arc resistance | ASTM D495 | 5 | PLC | |
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 80 | ||
| Drying Time | hr | 2～4 | ||
| Water Content Control | % | ≤0.2 | ||
| Melt Temperature Optimum | ℃ | 215 | ||
| Min. Melt Temperature | ℃ | 210 | ||
| Max. Melt Temperature | ℃ | 220 | ||
| Mould Temperature | ℃ | 90 | ||
| Min. Mould Temperature | ℃ | 80 | ||
| Max. Mould Temperature | ℃ | 100 | ||
| Screw speed | ℃ | * | ||
| Holding Pressure | MPa | 80～110 | ||
| Hold Pressure Time | s/mm | 8 | ||
| Annealing Time | min/mm | 30 | ||
| Annealing Temperature | ℃ | 160 | ||
| Extrusion molding | ||||
| Dry Temperature | ℃ | * | ||
| Dry Time | hr | * | ||
| Water Content Control | % | * | ||
| Melt Temperature | ℃ | * | ||
| Melt Temperature Optimum | ℃ | * | ||
Low friction. General purpose grade /Thin wall products
Learn More
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ