Home > Product > Raw Material > POM
| Material Technical Datasheet | ||||
| PC650 NC010 | ||||
| FEATURES | APPLICATIONS | |||
| Low friction | ||||
| Lubricated | ||||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Density | ISO 1183 | kg/m³ | 1420 | |
| Shrinkage Flow | ISO 294 | % | 2 | |
| Shrinkage xFlow | ISO 294 | % | 1.9 | |
| Water Absorption | ISO 62 | 2.00mm | % | 1.4 |
| Water Absorption | ISO 62 | 24hr In Water | % | 0.3 |
| Melt Index | ISO 1133 | 190℃2.16kg | cm³/10min | 13 |
| Melt Index | ISO 1133 | 190℃2.16kg | g/10min | 15 |
| Melt Density | INTERNAL METHOD | kg/m³ | * | |
| Hardness | ||||
| Rockwell Hardness M(Scale) | ISO 2039 | 92 | ||
| Rockwell Hardness R(Scale) | ISO 2039 | 120 | ||
| Ball Indentation Hardness | ISO 2039 | H961/30 | * | |
| Mechanical Properties | ||||
| Tensile Modulus | ISO 527 | Mpa | 3100 | |
| Tensile Strength | ISO 527 | Mpa | 71 | |
| Elongation Yield | ISO 527 | % | 17 | |
| Elongation Break | ISO 527 | % | 30 | |
| Poisson Ratio | INTERNAL METHOD | 0.37 | ||
| Tensile Creep Modulus | ISO 899 | 1hr | Mpa | 2800 |
| Tensile Creep Modulus | ISO 899 | 1000hr | Mpa | 1600 |
| Flexural Strength | ISO 178 | 3.5%Strain | Mpa | 80 |
| Flexural Modulus | ISO 178 | Mpa | 2950 | |
| lzod Notch lmpact | ISO 180 | 23'℃Type A | kJ/㎡ | 9 |
| Izod Notch lmpact | ISO 180 | -40°CType A | kJ/㎡ | 8 |
| lzod un-Notch lmpact | ISO 180 | 23'℃Type A | kJ/㎡ | 280 |
| Izod un-Notch lmpact | ISO 180 | -40°CType A | kJ/㎡ | 250 |
| Charpy Notch lmpact | ISO 179 | 23°C1eA | kJ/㎡ | 9 |
| Charpy Notch lmpact | ISO 179 | -30°C1eA | kJ/㎡ | 8 |
| Charpy Un-notch lmpact | ISO 179 | 23°C | kJ/㎡ | 320 |
| CharpyUn-notch lmpact | ISO 179 | -30°C | kJ/㎡ | 280 |
| Friction Coefficient Dynamic VS | ASTM D1894 | 1HR | * | |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| HDT 1.8MPa | ISO 75 | 1.8MPa 6.4mm | ℃ | 95 |
| HDT 0.45MPa | ISO 75 | ℃ | 160 | |
| Vicat softeningTemperature | ISO 306 | 50°C/hr 50N | ℃ | 155 |
| Melting Temperature | ISO 11357 | 10°C/min | ℃ | 178 |
| CLE FIow | ISO 11359 | m/m/K | 1.10E-04 | |
| CLE xFlow | ISO 11359 | m/m/K | 1.10E-04 | |
| CLE FIow | ISO 11359 | ‘-40~23℃ | m/m/K | * |
| CLE xFlow | ISO 11359 | ‘-40~23℃ | m/m/K | * |
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Flame Rating All Color 0.75mm | UL94 | * | ||
| Flame Rating All Color 1.5mm | UL94 | * | ||
| Flame Rating All Color 0.8mm | UL94 | * | ||
| Buming Rate 1.00mm | ISO 3795 | * | MM/MIN | |
| Electrical Performance | ||||
| Electrical Performance | Test Standard | * | Units | |
| Volume Resistivity | IEC 62631 | 2.00E+12 | Ω.m | |
| Surface Resistivity | IEC 62631-3-2 | 4.00E+14 | Ω | |
| DielectricStrength | IEC 60243 | 44 | KV/mm | |
| Dielectric Constant 100Hz | IEC 62631-2-1 | 3.8 | ||
| Dielectric Constant 1Hz | IEC 62631-2-1 | 3.8 | ||
| Dissipation Factor 100MHz | IEC 62631-2-1 | 0.009 | ||
| Dissipation Factor 1MHz | IEC 62631-2-1 | 0.0055 | ||
| CTl | 60112 | 600 | V | |
| VDA Properties | ||||
| Emission | VDA 275 | 8 | MG/KG | |
| Emission of organic compounds | VDA 275 | * | μm/g | |
| Fogging F-value Condenate | ISO 6452 | 90 | % | |
| Fogging G-value Condenate | ISO 6452 | 0.35 | mg | |
| UL | ||||
| Flame Retardancy | Test Standard | Data | Units | |
| UL FlameRating ALL 0.75mm | UL94 | * | ||
| HWI ALL0.75mm | UL 746A | * | PLC | |
| HWI ALL0.75mm | UL 746A | * | PLC | |
| RTI Elec ALL0.75mm | UL746B | * | ℃ | |
| RTI lmp ALL 0.75mm | UL746B | * | ℃ | |
| RTI Str ALL 0.75mm | UL746B | * | ℃ | |
| UL FlameRating ALL 1.5mm | UL94 | * | ||
| HWI ALL1.5mm | UL 746A | * | PLC | |
| HWI ALL1.5mm | UL 746A | * | PLC | |
| RTI Elec ALL1.5mm | UL746B | * | ℃ | |
| RTI lmp ALL 1.5mm | UL746B | * | ℃ | |
| RTI Str ALL 1.5mm | UL746B | * | ℃ | |
| UL FlameRating ALL 3.0mm | UL94 | * | ||
| HWI ALL3.0mm | UL 746A | * | PLC | |
| HWI ALL3.0mm | UL 746A | * | PLC | |
| RTI Elec ALL3.0mm | UL746B | * | ℃ | |
| RTI lmp ALL 3.0mm | UL746B | * | ℃ | |
| RTI Str ALL 3.0mm | UL746B | * | ℃ | |
| UL FlameRating ALL6.0mm | UL94 | * | ||
| HWI ALL6.0mm | UL 746A | * | PLC | |
| HWI ALL6.0mm | UL 746A | * | PLC | |
| RTI Elec ALL6.0mm | UL746B | * | ℃ | |
| RTI lmp ALL 6.0mm | UL746B | * | ℃ | |
| RTI Str ALL 6.0mm | UL746B | * | ℃ | |
| CTI | IEC 60112 | * | PLC | |
| HVTR | UL 746A | * | PLC | |
| Arc resistance | ASTM D495 | * | PLC | |
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 80 | ||
| Drying Time | hr | 2～4 | ||
| Water Content Control | % | ≤0.2 | ||
| Melt Temperature Optimum | ℃ | 215 | ||
| Min. Melt Temperature | ℃ | 210 | ||
| Max. Melt Temperature | ℃ | 220 | ||
| Mould Temperature | ℃ | 90 | ||
| Min. Mould Temperature | ℃ | 80 | ||
| Max. Mould Temperature | ℃ | 100 | ||
| Screw speed | ℃ | * | ||
| Holding Pressure | MPa | 80～110 | ||
| Hold Pressure Time | s/mm | 8 | ||
| Annealing Time | min/mm | 30 | ||
| Annealing Temperature | ℃ | 160 | ||
| Extrusion molding | ||||
| Dry Temperature | ℃ | * | ||
| Dry Time | hr | * | ||
| Water Content Control | % | * | ||
| Melt Temperature | ℃ | * | ||
| Melt Temperature Optimum | ℃ | * | ||
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.