Home > Product > Raw Material > POM
| Material Technical Datasheet | ||||
| 500MT NC010 | ||||
| FEATURES | APPLICATIONS | |||
| Low friction | ||||
| Lubricated | ||||
| Ultrasonic welding | ||||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Density | ASTM D792 | kg/m³ | 1350 | |
| shrinkage flow | ASTM D955 | % | 1.4 | |
| shrinkage xflow | ASTM D955 | % | 1.5 | |
| Water Absorption | ASTM D570 | 23'℃ 24hr | % | 1.9 |
| Water Absorption | ASTM D570 | % | 0.3 | |
| Melt Index | ISO 1133 | 190℃2.16kg | cm³/10min | 8 |
| Melt IDensity | kg/m³ | * | ||
| Hardness | ||||
| Rockwell Hardness M(Scale) | ASTM D785 | * | ||
| Rockwell Hardness R(Scale) | ASTM D785 | * | ||
| Mechanical Properties | ||||
| Tensile Modulus | ASTM D638 | 23'℃ | Mpa | 1600 |
| Tensile Strength | ASTM D638 | 23'℃ | Mpa | 43 |
| Elongation | ASTM D638 | ’-55℃ | % | 22 |
| Elongation | ASTM D638 | 23'℃ | % | 42 |
| Flexural Modulus | ASTM D790 | 23'℃ | Mpa | * |
| lzod Notch lmpact | ASTM D790 | 23'℃ | Mpa | * |
| lzod un-Notch lmpact | ASTM D790 | 23'℃ | Mpa | * |
| Charpy Notch lmpact | ISO 179 | 23°C1eA | kJ/m³ | 20 |
| Charpy Notch lmpact | ISO 179 | -30°C1eA | kJ/m³ | 10 |
| Charpy Un-notch lmpact | ISO 179 | 23°C | kJ/m³ | NB |
| CharpyUn-notch lmpact | ISO 179 | -30°C | kJ/m³ | NB |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| HDT 1.8MPa | ASTM D638 | 1.8MPa 6.4mm | ℃ | 66 |
| HDT 0.45MPa | ASTM D638 | ℃ | 127 | |
| Melting Temperature | 10°C/min | ℃ | 178 | |
| CLE FIow | ASTM D696 | cm/cm/℃ | 1.30E-04 | |
| Specific Heat | ASTM C351 | J/(kg℃） | 1.30E-04 | |
| Electrical Performance | ||||
| Volume Resistivity | ASTM D257 | * | Ω.m | |
| flammability | ||||
| Limiting Oxygen Index | ISO 4589 | 20 | % | |
| Flame Rating All Color 0.75mm | UL94 | * | ||
| Flame Rating All Color 1.5mm | UL94 | * | ||
| Flame Rating All Color 3.0mm | UL94 | * | ||
| UL | ||||
| Flame Retardancy | Test Standard | Data | Units | |
| UL FlameRating ALL 0.75mm | UL94 | * | ||
| HWI ALL0.75mm | UL 746A | * | PLC | |
| HWI ALL0.75mm | UL 746A | * | PLC | |
| RTI Elec ALL0.75mm | UL746B | * | ℃ | |
| RTI lmp ALL 0.75mm | UL746B | * | ℃ | |
| RTI Str ALL 0.75mm | UL746B | * | ℃ | |
| UL FlameRating ALL 1.5mm | UL94 | * | ||
| HWI ALL1.5mm | UL 746A | * | PLC | |
| HWI ALL1.5mm | UL 746A | * | PLC | |
| RTI Elec ALL1.5mm | UL746B | * | ℃ | |
| RTI lmp ALL 1.5mm | UL746B | * | ℃ | |
| RTI Str ALL 1.5mm | UL746B | * | ℃ | |
| UL FlameRating ALL 3.0mm | UL94 | * | ||
| HWI ALL3.0mm | UL 746A | * | PLC | |
| HWI ALL3.0mm | UL 746A | * | PLC | |
| RTI Elec ALL3.0mm | UL746B | * | ℃ | |
| RTI lmp ALL 3.0mm | UL746B | * | ℃ | |
| RTI Str ALL 3.0mm | UL746B | * | ℃ | |
| CTI | IEC 60112 | * | PLC | |
| HVTR | UL 746A | * | PLC | |
| Arc resistance | ASTM D495 | * | PLC | |
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ