Home > Product > Raw Material > POM
●FEATURES:Lubricated Low friction
●APPLICATIONS:profiles sheet
| Material Technical Datasheet | ||||
| 100KM NC000 | ||||
| FEATURES | APPLICATIONS | |||
| Low friction. | profiles | |||
| Lubricated | sheet | |||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Density | ISO 1183 | kg/m³ | 1410 | |
| Shrinkage Flow | ISO 294 | % | 1.8 | |
| Shrinkage xFlow | ISO 294 | % | 1.5 | |
| Melt Index | ISO 1133 | 190℃2.16kg | cm³/10min | 1.7 |
| Melt Index | ISO 1133 | 190℃2.16kg | g/10min | 2 |
| Melt IDensity | kg/m³ | 1180 | ||
| Mechanical Properties | ||||
| Tensile Modulus | ISO 527 | Mpa | 3100 | |
| Tensile Strength | ISO 527 | Mpa | 65 | |
| Elongation Break | ISO 527 | % | 15 | |
| Poisson Ratio | ISO 527 | 0.37 | ||
| Flexural Modulus | ISO 178 | Mpa | 3000 | |
| Charpy Notch lmpact | ISO 179 | 23°C1eA | kJ/m³ | 4.5 |
| Charpy Notch lmpact | ISO 179 | -30°C1eA | kJ/m³ | 3.5 |
| Charpy Un-notch lmpact | ISO 179 | 23°C | kJ/m³ | 50 |
| CharpyUn-notch lmpact | ISO 179 | -30°C | kJ/m³ | 60 |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| HDT 1.8MPa | ISO 75 | 1.8MPa 6.4mm | ℃ | 98 |
| HDT 0.45MPa | ISO 75 | ℃ | 160 | |
| Vicat softeningTemperature | ISO 306 | 50°C/hr 50N | ℃ | _ |
| Vicat softeningTemperature | ISO 306 | 50°C/hr 10N | ℃ | _ |
| Melting Temperature | ISO 11357 | 10°C/min | ℃ | 178 |
| CLE FIow | ISO 11359 | m/m/K | 1.10E-04 | |
| CLE xFIow | ISO 11359 | m/m/K | 1.00E-04 | |
| CLE FIow | ISO 11359 | -40~23°C | m/m/K | 9.20E-05 |
| CLE xFlow | ISO 11359 | -40~23°C | m/m/K | 9.40E-05 |
| Flame Retardancy | ||||
| FMVSS Class | ISO 3795 | mm/min | B | |
| VDA Properties | ||||
| Emission | VDA 275 | mg/kg | 8 | |
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 80 | ||
| Drying Time | hr | 2～4 | ||
| Water Content Control | % | ≤0.2 | ||
| Melt Temperature Optimum | ℃ | 215 | ||
| Min. Melt Temperature | ℃ | 210 | ||
| Max. Melt Temperature | ℃ | 220 | ||
| Mould Temperature | ℃ | 90 | ||
| Min. Mould Temperature | ℃ | 80 | ||
| Max. Mould Temperature | ℃ | 100 | ||
| Screw Speed | m/s | 0.2 | ||
| Holding Pressure | MPa | 90～110 | ||
| Hold Pressure Time | s/mm | 8 | ||
| Annealing Time | min/mm | 30 | ||
| Annealing Temperature | ℃ | 160 | ||
| Extrusion molding | ||||
| Dry Temperature | ℃ | 75~85 | ||
| Dry Time | hr | 2~4 | ||
| Water Content Control | % | ≤0.2 | ||
| Melt Temperature | ℃ | 195~205 | ||
| Melt Temperature Optimum | ℃ | 200 | ||
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ