| Material Technical Datasheet | ||||
| 520MP NC010 | ||||
| FEATURES | APPLICATIONS | |||
| Low friction. | ||||
| Lubricated | ||||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Density | ISO 1183 | kg/m³ | 1540 | |
| Shrinkage Flow | ISO 294 | % | 1.9 | |
| Shrinkage xFlow | ISO 294 | % | 1.5 | |
| Melt Index | ISO 1133 | 190℃2.16kg | g/10min | 8 |
| Hardness | ||||
| Rockwell Hardness M(Scale) | ISO 2039 | 85 | ||
| Rockwell Hardness R(Scale) | ISO 2039 | 121 | ||
| Mechanical Properties | ||||
| Tensile Modulus | ISO 527 | Mpa | 2800 | |
| Tensile Strength | ISO 527 | Mpa | 53 | |
| Elongation Yield | ISO 527 | % | 13 | |
| Elongation Break | ISO 527 | % | 15 | |
| Poisson Ratio | ISO 527 | 0.37 | ||
| Tensile Creep Modulus | ISO 899 | 1hr | Mpa | 1500 |
| Tensile Creep Modulus | ISO 899 | 1000hr | Mpa | 800 |
| Flexural Modulus | ISO 178 | Mpa | 2700 | |
| lzod Notch lmpact | ISO 180 | 23'℃Type A | kJ/m³ | 4 |
| Charpy Notch lmpact | ISO 179 | 23°C1eA | kJ/m³ | 4 |
| Charpy Notch lmpact | ISO 179 | -30°C1eA | kJ/m³ | 4 |
| Charpy Un-notch lmpact | ISO 179 | 23°C | kJ/m³ | 70 |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| HDT 1.8MPa | ISO 75 | 1.8MPa 6.4mm | ℃ | 94 |
| HDT 0.45MPa | ISO 75 | ℃ | 160 | |
| Melting Temperature | ISO 11357 | 10°C/min | ℃ | 178 |
| CLE FIow | ISO 11359 | m/m/K | 1.00E-04 | |
| CLE xFlow | ISO 11359 | m/m/K | 1.00E-04 | |
| CLE FIow -40~23℃ | ISO 11359 | m/m/K | 9.00E-05 | |
| CLE xFlow -40~23℃ | ISO 11359 | m/m/K | 9.00E-05 | |
| Flame Retardancy | ||||
| Flame Rating All Color 1.5mm | UL94 | HB | ||
| Flame Rating All Color 3.0mm | UL94 | HB | ||
| Buming Rate | ISO 3795 | 37 | mm/min | |
| VDA Properties | ||||
| Emission | VDA 275 | 8 | mg/kg | |
| UL | ||||
| Flame Retardancy | Test Standard | Data | Units | |
| UL FlameRating ALL 1.5mm | UL94 | HB | ||
| HWI ALL1.5mm | UL 746A | 3 | PLC | |
| HWI ALL1.5mm | UL 746A | 0 | PLC | |
| RTI Elec ALL1.5mm | UL746B | 105 | ℃ | |
| RTI lmp ALL 1.5mm | UL746B | 85 | ℃ | |
| RTI Str ALL 1.5mm | UL746B | 90 | ℃ | |
| UL FlameRating ALL 3.0mm | UL94 | HB | ||
| HWI ALL3.0mm | UL 746A | 2 | PLC | |
| HWI ALL3.0mm | UL 746A | 0 | PLC | |
| RTI Elec ALL3.0mm | UL746B | 105 | ℃ | |
| RTI lmp ALL 3.0mm | UL746B | 85 | ℃ | |
| RTI Str ALL 3.0mm | UL746B | 90 | ℃ | |
| CTI | IEC 60112 | 0 | PLC | |
| HVTR | UL 746A | 0 | PLC | |
| Arc resistance | ASTM D495 | 4 | PLC | |
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 80 | ||
| Drying Time | hr | 2～4 | ||
| Water Content Control | % | ≤0.2 | ||
| Melt Temperature Optimum | ℃ | 215 | ||
| Min. Melt Temperature | ℃ | 210 | ||
| Max. Melt Temperature | ℃ | 220 | ||
| Mould Temperature | ℃ | 90 | ||
| Min. Mould Temperature | ℃ | 80 | ||
| Max. Mould Temperature | ℃ | 100 | ||
| Holding Pressure | MPa | 80～100 | ||
| Hold Pressure Time | s/mm | 8 | ||
| Annealing Time | min/mm | 30 | ||
| Annealing Temperature | ℃ | 160 | ||
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ