●FEATURES:Low friction. Low EmissionLight satbilized LubricatedLow VOC
●APPLICATIONS:Profiles Sheet
| Material Technical Datasheet | ||||
| 127UVE NC010 | ||||
| FEATURES | APPLICATIONS | |||
| Low friction. | profile | |||
| Low Emission | sheet | |||
| Light satbilized | ||||
| Lubricated | ||||
| Low VOC | ||||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Density | ISO 1183 | kg/m³ | 1420 | |
| Shrinkage Flow | ISO 294 | % | 2.1 | |
| Shrinkage xFlow | ISO 294 | % | 1.9 | |
| Melt Index | ISO 1133 | 190℃2.16kg | cm³/10min | 2.1 |
| Melt Index | ISO 1133 | 190℃2.16kg | g/10min | 2.5 |
| Hardness | ||||
| Rockwell Hardness M(Scale) | ISO 2039 | 88.3 | ||
| Rockwell Hardness R(Scale) | ISO 2039 | 120 | ||
| Mechanical Properties | ||||
| Tensile Modulus | ISO 527 | Mpa | 2900 | |
| Tensile Strength | ISO 527 | Mpa | 71 | |
| Elongation Yield | ISO 527 | % | 25 | |
| Elongation Break | ISO 527 | % | 45 | |
| Poisson Ratio | ISO 527 | 0.37 | ||
| Flexural Stength | ISO 178 | 3.5%strain | 77.2 | |
| Flexural Modulus | ISO 178 | Mpa | 2800 | |
| lzod Notch lmpact | ISO 180 | 23'℃Type A | kJ/m³ | 12 |
| Izod Notch lmpact | ISO 180 | -40°CType A | kJ/m³ | 280 |
| Charpy Notch lmpact | ISO 179 | 23°C1eA | kJ/m³ | 14 |
| Charpy Notch lmpact | ISO 179 | -30°C1eA | kJ/m³ | 10 |
| Charpy Un-notch lmpact | ISO 179 | 23°C | kJ/m³ | 390 |
| CharpyUn-notch lmpact | ISO 179 | -30°C | kJ/m³ | 340 |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| HDT 1.8MPa | ISO 75 | 1.8MPa 6.4mm | ℃ | 91 |
| HDT 0.45MPa | ISO 75 | ℃ | 159 | |
| Vicat softeningTemperature | ISO 306 | 50°C/hr 50N | ℃ | 160 |
| Vicat softeningTemperature | ISO 306 | 50°C/hr 10N | ℃ | 174 |
| Melting Temperature | ISO 11357 | 10°C/min | ℃ | 178 |
| CLE FIow | ISO 11359 | m/m/K | 1.20E-04 | |
| CLE xFlow | ISO 11359 | m/m/K | 1.10E-04 | |
| Flame Retardancy | ||||
| Buming Rate | ISO 3795 | 27 | mm/min | |
| VDA Properties | ||||
| Emission | VDA 275 | 2 | mg/kg | |
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 80 | ||
| Drying Time | hr | 2～4 | ||
| Water Content Control | % | ≤0.2 | ||
| Melt Temperature Optimum | ℃ | 205 | ||
| Min. Melt Temperature | ℃ | 200 | ||
| Max. Melt Temperature | ℃ | 210 | ||
| Mould Temperature | ℃ | 90 | ||
| Min. Mould Temperature | ℃ | 80 | ||
| Max. Mould Temperature | ℃ | 100 | ||
| Holding Pressure | MPa | 90～110 | ||
| Hold Pressure Time | s/mm | 8 | ||
| Annealing Time | min/mm | 30 | ||
| Annealing Temperature | ℃ | 160 | ||
| Extrusion molding | ||||
| Dry Temperature | ℃ | 75~85 | ||
| Dry Time | hr | 2~4 | ||
| Water Content Control | % | ≤0.2 | ||
| Melt Temperature | ℃ | 195~205 | ||
| Melt Temperature Optimum | ℃ | 200 | ||
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ