Home > Product > Raw Material > POM
●FEATURES:Low friction Low Emissions Low VOCLubricated
●APPLICATIONS:profiles sheet
| Material Technical Datasheet | ||||
| 300TE BK602 | ||||
| FEATURES | APPLICATIONS | |||
| Low friction | Profiles | |||
| Low Emissions | Sheet | |||
| Low VOC | ||||
| Lubricated | ||||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Density | ISO 1183 | kg/m³ | 1370 | |
| Shrinkage Flow | ISO 294 | % | 1.3 | |
| Shrinkage xFlow | ISO 294 | % | 1.5 | |
| Melt Index | ISO 1133 | 190℃2.16kg | g/10min | 6 |
| Melt Density | INTERNAL METHOD | kg/m³ | 1150 | |
| Hardness | ||||
| Rockwell Hardness M(Scale) | ISO 2039 | 69 | ||
| Rockwell Hardness R(Scale) | ISO 2039 | 116 | ||
| Mechanical Properties | ||||
| Tensile Modulus | ISO 527 | Mpa | 2000 | |
| Tensile Strength | ISO 527 | Mpa | 54 | |
| Elongation Yield | ISO 527 | % | 20 | |
| Elongation Break | ISO 527 | % | 29 | |
| Poisson Ratio | INTERNAL METHOD | 0.4 | ||
| Flexural Strength | ISO 178 | 3.5%Strain | Mpa | 55 |
| Flexural Modulus | ISO 178 | Mpa | 2000 | |
| Charpy Notch lmpact | ISO 179 | 23°C1eA | kJ/m³ | 15 |
| Charpy Notch lmpact | ISO 179 | -30°C1eA | kJ/m³ | 8 |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| HDT 1.8MPa | ISO 75 | 1.8MPa 6.4mm | ℃ | 78 |
| HDT Annealed 1.8MPa | ISO 75 | 0.45MPa 6.4mm | ℃ | 136 |
| Vicat softeningTemperature | ISO 306 | 50°C/hr 10N | ℃ | 172 |
| CLE FIow | ISO 11359 | m/m/K | 1.10E-04 | |
| CLE xFlow | ISO 11359 | m/m/K | 1.20E-04 | |
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Buming Rate 1.00mm | ISO 3795 | 80 | mm/min | |
| VDA Properties | ||||
| Emission | VDA 275 | 2 | mg/kg | |
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 80 | ||
| Drying Time | hr | 4～8 | ||
| Water Content Control | % | ≤0.05 | ||
| Melt Temperature Optimum | ℃ | 205 | ||
| Min. Melt Temperature | ℃ | 200 | ||
| Max. Melt Temperature | ℃ | 210 | ||
| Mould Temperature | ℃ | 50 | ||
| Min. Mould Temperature | ℃ | 40 | ||
| Max. Mould Temperature | ℃ | 60 | ||
| Holding Pressure | MPa | 60～80 | ||
| Hold Pressure Time | s/mm | 7.5 | ||
| Annealing Time | min/mm | 30 | ||
| Annealing Temperature | ℃ | 160 | ||
| Extrusion molding | ||||
| Dry Temperature | ℃ | 75~85 | ||
| Dry Time | hr | 2~4 | ||
| Water Content Control | % | ≤0.05 | ||
| Melt Temperature | ℃ | 195~205 | ||
| Melt Temperature Optimum | ℃ | 200 | ||
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ