Home > Product > Raw Material > POM
●FEATURES:High modulusHigh tensile strength Low warpage Low voids
| Material Technical Datasheet | ||||
| 111P NC010 | ||||
| FEATURES | APPLICATIONS | |||
| High modulus | ||||
| High tensile strength | ||||
| Low warpage | ||||
| Low voids | ||||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Density | ISO 1183 | kg/m³ | 1420 | |
| Shrinkage Flow | ISO 294 | % | 2 | |
| Shrinkage xFlow | ISO 294 | % | 1.9 | |
| Water Absorption | ISO 62 | % | 1 | |
| Melt Index | ISO 1133 | 190℃2.16kg | g/10min | 2.4 |
| Hardness | ||||
| Rockwell Hardness M(Scale) | ISO 2039 | 92 | ||
| Rockwell Hardness R(Scale) | ISO 2039 | 120 | ||
| Mechanical Properties | ||||
| Tensile Modulus | ISO 527 | Mpa | 3200 | |
| Tensile Strength | ISO 527 | Mpa | 72 | |
| Elongation Yield | ISO 527 | % | 20 | |
| Elongation Break | ISO 527 | % | 35~50 | |
| Tensile Creep Modulus | ISO 899 | 1hr | Mpa | 3000 |
| Tensile Creep Modulus | ISO 899 | 1000hr | Mpa | 1700 |
| Flexural Strength | ISO 178 | 3.5%Strain | Mpa | 80 |
| Flexural Modulus | ISO 178 | Mpa | 2900 | |
| Charpy Notch lmpact | ISO 179 | 23°C1eA | kJ/m³ | 9 |
| Charpy Notch lmpact | ISO 179 | -30°C1eA | kJ/m³ | 11 |
| Charpy Un-notch lmpact | ISO 179 | 23°C | kJ/m³ | 270 |
| CharpyUn-notch lmpact | ISO 179 | -30°C | kJ/m³ | 300 |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| HDT 1.8MPa | ISO 75 | 1.8MPa 6.4mm | ℃ | 100 |
| HDT 0.45MPa | ISO 75 | ℃ | 165 | |
| Vicat softeningTemperature | ISO 306 | 50°C/hr 50N | ℃ | 160 |
| Melting Temperature | ISO 11357 | 10°C/min | ℃ | 178 |
| CLE xFlow -40.0~23℃ | ISO 11359 | cm/cm/℃ | 9.40E-05 | |
| CLE Flow -40.0~23℃ | ISO 11359 | cm/cm/℃ | 9.40E-05 | |
| CLE xFlow 23~55℃ | ISO 11359 | cm/cm/℃ | 1.41E-04 | |
| CLE Flow 23~55℃ | ISO 11359 | cm/cm/℃ | 1.30E-04 | |
| CLE xFlow 55~100℃ | ISO 11359 | cm/cm/℃ | 1.41E-04 | |
| CLE Flow 55~100℃ | ISO 11359 | cm/cm/℃ | 1.30E-04 | |
| Electrical Performance | ||||
| CTl | 60112 | 600 | V | |
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Flame Rating All Color 1.5mm | UL94 | HB | ||
| Flame Rating All Color 3.0mm | UL94 | HB | ||
| Limiting Oxygen Index | ISO4589 | 17 | % | |
| UL | ||||
| Flame Retardancy | Test Standard | Data | Units | |
| UL FlameRating ALL 1.5mm | UL94 | HB | ||
| HWI ALL1.5mm | UL 746A | 4 | PLC | |
| HWI ALL1.5mm | UL 746A | 0 | PLC | |
| RTI Elec ALL1.5mm | UL746B | 110 | ℃ | |
| RTI lmp ALL 1.5mm | UL746B | 85 | ℃ | |
| RTI Str ALL 1.5mm | UL746B | 90 | ℃ | |
| UL FlameRating ALL 3.0mm | UL94 | HB | ||
| HWI ALL3.0mm | UL 746A | 3 | PLC | |
| HWI ALL3.0mm | UL 746A | 0 | PLC | |
| RTI Elec ALL3.0mm | UL746B | 110 | ℃ | |
| RTI lmp ALL 3.0mm | UL746B | 90 | ℃ | |
| RTI Str ALL 3.0mm | UL746B | 95 | ℃ | |
| CTI | IEC 60112 | 0 | PLC | |
| HVTR | UL 746A | 0 | PLC | |
| Arc resistance | ASTM D495 | 5 | PLC | |
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 80 | ||
| Drying Time | hr | 2～4 | ||
| Water Content Control | % | ≤0.2 | ||
| Melt Temperature | ℃ | 210~220 | ||
| Melt Temperature Optimum | ℃ | 215 | ||
| Mould Temperature | ℃ | 90 | ||
| Min. Mould Temperature | ℃ | 80 | ||
| Max. Mould Temperature | ℃ | 100 | ||
| Screw Speed | m/s | 0.2 | ||
| Holding Pressure | MPa | 90～100 | ||
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ