Home > Product > Modified Material > PBT > PC/PBT
● Material shape: granular
● Processing method: injection molding
● Flame retardant grade: HB
● Material properties: alloy
● Compliance: UL
● Material characteristics: high fluidity, chemical resistance, good weather resistance, good processability
● Material use: household equipment, commercial equipment, large products, injection molding applications
| Material Technical Datasheet | ||||
| K01 | ||||
| PROPERTY | ||||
| Alloy | ||||
| FEATURES | APPLICATIONS | |||
| High fluidity | Household equipment | |||
| Chemical resistance | Commercial equipment | |||
| Good weather resistance | Large products | |||
| Good processability | Injection molding applications | |||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Specific Gravity | ASTM D792 | 23℃ | g/cm³ | 1.22 |
| Shrinkage Rate | ASTM D995 | 23℃ | % | 0.6~1.0 |
| Melt index 230°C 5kg | ASTM D1238 | 23 ℃ | g/10min | 28 |
| Mechanical Properties | ||||
| Mechanical Properties | Test Standard | Test Condition | Units | Data |
| Tensile Strength | ASTM D638 | 50mm/min | Mpa | 55 |
| Elongation | ASTM D638 | 50mm/min | % | 80 |
| Flexural Strength | ASTM D790 | 2.0mm/min | Mpa | 80 |
| Flexural Modulus | ASTM D790 | 2.0mm/min | Mpa | 2100 |
| Cantilever notch impact 23°C 3.2mm | ASTM D256 | 23 ° C A-notch | J/m | 660 |
| Cantilever without notch impact 23°C 3.2mm | ASTM D256 | 23 ° C A-notch | J/m | NB |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| H.D.T | ASTM D648 | 0.45MPa | ℃ | 107 |
| H.D.T | ASTM D648 | 1.8MPa | ℃ | 95 |
| Electrical Performance | ||||
| Electrical Performance | Test Standard | Data | Units | |
| Volume resistance | ASTM D257 | 1E16 | Ω.cm | |
| Surface resistance | ASTM D257 | 1E15 | Ω | |
| Insulation strength | ASTM D149 | 28 | KV/mm | |
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Fire Rating Full Color 1.5mm | UL94 | HB | ||
| Fire Rating Full Color 3.0mm | UL94 | HB | ||
| UL | ||||
| Flame Retardancy | Test Standard | Data | Units | |
| Fire Rating Full Color 1.5mm | UL94 | HB | ||
| Fire Rating Full Color 3.0mm | UL94 | HB | ||
| HWI Full color 1.5mm | UL 746A | 4 | PLC | |
| HWI Full color 3.0mm | UL 746A | 2 | PLC | |
| HAI Full color 1.5mm | UL 746A | 0 | PLC | |
| HAI Full color 3.0mm | UL 746A | 0 | PLC | |
| RTI Elec Full color 1.5mm | UL 746B | 50 | °C | |
| RTI Elec Full color 3.0mm | UL 746B | 50 | °C | |
| RTI Imp Full color 1.5mm | UL 746B | 50 | °C | |
| RTI Imp Full color 3.0mm | UL 746B | 50 | °C | |
| RTI Str Full color 1.5mm | UL 746B | 50 | °C | |
| RTI Str Full color 3.0mm | UL 746B | 50 | °C | |
| CTI | IEC 60112 | 0 | PLC | |
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 120 | ||
| Drying Time | h | 4~6 | ||
| Front Temperature | ℃ | 220~240 | ||
| Middle Temperature | ℃ | 230~250 | ||
| Temperature of The Third Section | ℃ | 240~260 | ||
| Melting temperature | ℃ | 220~260 | ||
| Maximum melting temperature | ℃ | 280 | ||
| Mold Temperature | ℃ | 60~100 | ||
| Injection speed | Low speed to high speed | |||
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ