| Material Technical Datasheet | ||||
| PA66 AKV30 000000 | ||||
| FEATURES | APPLICATIONS | |||
| Properties | Test Standard | Units | Values | |
| Physical Properties | ||||
| Specific Gravity | ISO 1183 | kg/m³ | 1360 | |
| Shrinkage Flow 150x105x3mm 290'C 40MPa Mold temperature:80°C | ISO 2577 | % | 0.35 | |
| Shrinkage xFlow 150x105x3mm 290'C 40MPa Moldtemperature:80°C | ISO 2577 | % | 1.46 | |
| Shrinkage Flow 150x105x3mm 120'C 4hr | ISO 2577 | % | 0.04 | |
| Shrinkage xFlow 150x105x3mm 120'C 4hr | ISO 2577 | % | 0.05 | |
| Hardness | ||||
| Dry | Wet | |||
| Ball Indentation Hardness | ISO 2039 | N/mm2 | 230 | 130 |
| Mechanical Properties | ||||
| Dry | Wet | |||
| Tensile Modulus 1.0mm/min | ISO 527 | Mpa | 10600 | 7000 |
| Tensile Strength break 5mm/min | ISO 527 | Mpa | 185 | 125 |
| Elongation Break 5mm/min | ISO 527 | % | 3 | 6 |
| Flexural Strength 2.0mm/min | ISO 178 | Mpa | 290 | 200 |
| Flexural Strength 3.5%Strain 2.0mm/min | ISO 178 | Mpa | 165 | |
| Flexural Modulus 2.0mm/min | ISO 178 | Mpa | 8400 | 5900 |
| Flexural Strain 2.0mm/min | ISO 178 | % | 4 | 6 |
| Izod Notch lmpact -30℃ | ISO 180 | KJ/m2 | 10 | 10 |
| Izod Notch lmpact -40℃ | ISO 180 | KJ/m2 | 10 | 10 |
| Charpy Notch lmpact 23°C | ISO 179 | KJ/m2 | 10 | 15 |
| Charpy Notch lmpact -30°C | ISO 179 | KJ/m2 | 10 | 10 |
| Charpy Un-notch lmpact 23°C | ISO 179 | KJ/m2 | 90 | 90 |
| Charpy Un-notch lmpact -30°C | ISO 179 | KJ/m2 | 70 | 70 |
| Thermal Properties | ||||
| Properties | Test Standard | Units | Value | |
| HDT 0.45MPa | ISO 75 | ℃ | 250 | |
| HDT 1.8MPa | ISO 75 | ℃ | 250 | |
| Vicat SofteningTemperature 120°C/hr 50N | ISO 306 | ℃ | 230 | |
| Melting Temperature:10'C/min | ISO 11357 | ℃ | 263 | |
| CLE Flow 23~55°C | ISO 11357 | m/m/K | 2.5E -5 | |
| CLE xFlow 23~55°C | ISO 11359 | m/m/K | 1E -4 | |
| Electrical Performance | ||||
| Electrical Performance | Test Standard | Data | Units | |
| Volume Resistivity | IEC 60093 | Ω.cm | 1E 13 | 1E 10 |
| Surface Resistivity | IEC 60093 | Ω | 1E 14 | 1E 13 |
| Dielectric Strength 1.0mm | IEC 60243 | KV/mm | 40 | 35 |
| CTl Solution A | IEC 60112 | V | 600 | |
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Fire Rating NC 1.5mm | UL94 | V-0 | ||
| UL | ||||
| Flame Retardancy | Test Standard | Data | Units | |
| Fire Rating NC 0.75mm | UL94 | V-0 | ||
| HWI NC 0.75mm | UL 746A | 4 | PLC | |
| HAI NC 0.75mm | UL 746A | 0 | PLC | |
| RTI Elec NC 0.75mm | UL 746B | 65 | °C | |
| RTI Imp NC 0.75mm | UL 746B | 65 | °C | |
| RTI Str NC 0.75mm | UL 746B | 65 | °C | |
| Injection molding | ||||
| Injection molding | Data | Units | ||
| Dry Temperature | 80 | °C | ||
| Dry Time | 2~6 | hr | ||
| Water Content Control | ≤0.12 | % | ||
| Melt Temperature | 280-300 | °C | ||
| Mould Temperature | 80-120 | °C | ||
High CTl /Auto connector "Automotive parts ,Office Applications
Learn More
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ