| Material Technical Datasheet | ||||
| PA66 AKV35H2.0 901510 | ||||
| FEATURES | APPLICATIONS | |||
| Heat Aging resistant | ||||
| Properties | Test Standard | Units | Values | |
| Physical Properties | ||||
| Specific Gravity | ISO 1183 | kg/m³ | 1410 | |
| Shrinkage Flow 60x60x2mm 290'C 60MPa Mold temperature:80°C | ISO 294 | % | 0.37 | |
| Shrinkage xFlow 60x60x2mm 290'C 50MPa Moldtemperature:80°C | ISO 294 | % | 0.91 | |
| Shrinkage Flow 60x60x2mm 120'C 4hr | ISO 294 | % | 0.05 | |
| Shrinkage xFlow 60x60x2mm 120'C 4hr | ISO 294 | % | 0.07 | |
| Hardness | ||||
| Dry | Wet | |||
| Ball indentation Hardness | ISO 2039 | 220 | 140 | |
| Mechanical Properties | ||||
| Dry | Wet | |||
| Tensile Modulus 1.0mm/min | ISO 527 | Mpa | 11200 | 7500 |
| Tensile Strength break 5mm/min | ISO 527 | Mpa | 200 | 125 |
| Elongation Break 5mm/min | ISO 527 | % | 3.1 | 6.4 |
| Flexural Strength 2.0mm/min | ISO 178 | Mpa | 300 | 200 |
| Flexural Strength 3.5%Strain 2.0mm/min | ISO 178 | Mpa | 280 | 165 |
| Flexural Modulus 2.0mm/min | ISO 178 | Mpa | 10500 | 6500 |
| Flexural Strain 2.0mm/min | ISO 178 | % | 4.1 | 6.2 |
| Izod Notch lmpact 23℃ | ISO 180 | KJ/m2 | 12 | 15 |
| Izod Notch lmpact -30℃ | ISO 180 | KJ/m2 | 10 | 10 |
| Izod Un-notch lmpact 23°C | ISO 180 | KJ/m2 | 75 | |
| Izod Un-notch lmpact -30°C | ISO 180 | KJ/m2 | 65 | |
| Charpy Notch lmpact 23°C 1eA | ISO 179 | KJ/m2 | 12 | 17 |
| Charpy Notch lmpact -30°C 1eA | ISO 179 | KJ/m2 | 10 | 10 |
| Charpy Un-notch lmpact 23°C | ISO 179 | KJ/m2 | 85 | 90 |
| Charpy Un-notch lmpact -30C | ISO 179 | KJ/m2 | 70 | 75 |
| Thermal Properties | ||||
| Properties | Test Standard | Units | Value | |
| HDT 0.45MPa | ISO 75 | ℃ | 250 | |
| HDT 1.8MPa | ISO 75 | ℃ | 250 | |
| Melting Temperature:10'C/min | ISO 11357 | ℃ | 263 | |
| CLE Flow 23~55°C | ISO 11357 | m/m/K | 3E -5 | |
| CLE xFlow 23~55°C | ISO 11359 | m/m/K | 9E -5 | |
| Electrical Performance | ||||
| Electrical Performance | Test Standard | Data | Units | |
| Volume Resistivity | IEC 60093 | 21E+13 | Ω.cm | |
| Surface Resistivity | IEC 60093 | 1E+15 | Ω | |
| Dielectric Strength 1.0mm | IEC 60243 | 35 | KV/mm | |
| CTl Solution A | IEC 60112 | 425 | V | |
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Fire Rating ALL 1.5mm | UL94 | HB | ||
| UL | ||||
| Flame Retardancy | Test Standard | Data | Units | |
| Fire Rating ALL 1.5mm | UL94 | HB | ||
| HWI ALL 1.5mm | UL 746A | 4 | PLC | |
| HAI ALL 1.5mm | UL 746A | 0 | PLC | |
| RTI Elec ALL 1.5mm | UL 746B | 120 | °C | |
| RTI Imp ALL1.5mm | UL 746B | 105 | °C | |
| RTI Str ALL 1.5mm | UL 746B | 115 | °C | |
| Injection molding | ||||
| Injection molding | Data | Units | ||
| Dry Temperature | 80 | °C | ||
| Dry Time | 2~6 | hr | ||
| Water Content Control | ≤0.12 | % | ||
| Melt Temperature | 280-300 | °C | ||
| Mould Temperature | 80-120 | °C | ||
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ