● Material shape: granular
● Processing method: injection molding
● Flame retardant grade :HB
● Compliance: UL
● Material characteristics: high gloss and high impact
● Material use: electronic products cabinet, household goods, ABS replacement
| Material Technical Datasheet | ||||
| HIPS HG K01 | ||||
| PROPERTY | ||||
| Flame retardant heat stable level | ||||
| FEATURES | APPLICATIONS | |||
| Good electrical performance | Electronics cabinet | |||
| High impact | Household items | |||
| Alternative ABS | ||||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Specific Gravity 23°C | ISO 1183 | 23℃ | g/cm³ | 1.04 |
| Shrinkage Rate Flow 23°C | ISO 2577 | 23℃ | % | 0.4~0.7 |
| Melt index 230°C 5kg | ISO 1133 | 23℃ | % | 5 |
| Mechanical Properties | ||||
| Mechanical Properties | Test Standard | Test Condition | Units | Data |
| Tensile Strength 50mm/min | ISO 527 | 50mm/min | Mpa | 32 |
| Elongation at Break 50mm/min | ISO 527 | 50mm/min | % | 30 |
| Flexural Strength 2.0mm/min | ISO 178 | 2.0mm/min | Mpa | 55 |
| Flexural Modulus 2.0mm/min | ISO 178 | 2.0mm/min | Mpa | 2100 |
| Cantilever notch impact 23°C | ISO 180 | 23 ° C A-notch | kJ/m² | 10 |
| Optical Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| Glossiness 60° 23°C | ASTM D523 | 95 | ||
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| Thermal deformation temperature | ISO 75 | 0.45MPa | ℃ | 73 |
| Vica softening temperature | ISO 306 | 1.8MPa | ℃ | 100 |
| Electrical Performance | ||||
| Electrical Performance | Test Standard | Data | Units | |
| Volume resistance | IEC 60093 | 1E16 | Ω.cm | |
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Fire Rating Full Color 1.3mm | UL94 | HB | ||
| Fire Rating Full Color 1.6mm | UL94 | HB | ||
| Fire Rating Full Color 3.2mm | UL94 | HB | ||
| UL | ||||
| Flame Retardancy | Test Standard | Data | Units | |
| Fire Rating Full Color 1.3mm | UL94 | HB | ||
| Fire Rating Full Color 1.6mm | UL94 | HB | ||
| Fire Rating Full Color 3.2mm | UL94 | HB | ||
| HWI Full color 1.6mm | UL 746A | 3 | PLC | |
| HWI Full color 3.2mm | UL 746A | 3 | PLC | |
| HAI Full color 1.6mm | UL 746A | 1 | PLC | |
| HAI Full Color 3.3mm | UL 746A | 0 | PLC | |
| RTI Elec Full color 1.2mm | UL 746B | 50 | °C | |
| RTI Elec Full color 1.6mm | UL 746B | 50 | °C | |
| RTI Elec Full color 3.2mm | UL 746B | 50 | °C | |
| RTI Imp Full color 1.2mm | UL 746B | 50 | °C | |
| RTI Imp Full color 1.6mm | UL 746B | 50 | °C | |
| RTI Imp Full color 3.2mm | UL 746B | 50 | °C | |
| RTI Str Full color 1.2mm | UL 746B | 50 | °C | |
| RTI Str Full color 1.6mm | UL 746B | 50 | °C | |
| RTI Str Full color 3.2mm | UL 746B | 50 | °C | |
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 70~80 | ||
| Drying Time | hr | 2~4 | ||
| Front Temperature | ℃ | 180~210 | ||
| Middle Temperature | ℃ | 200~230 | ||
| Temperature of The Third Section | ℃ | 210~240 | ||
| Melting temperature | ℃ | 210~240 | ||
| Maximum melting temperature | ℃ | 250 | ||
| Mold Temperature | ℃ | 30~80 | ||
| Injection speed | Low to medium speed | |||
| Back pressure | KPa | 0.0~1000 | ||
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ