V-1 V-0 Flame retardant grade 10% glass fiber reinforced pp plastic granules

● Material shape: granular

● Processing method: injection molding

● Flame retardant grade: V-1 V-0

● Material properties: 10% glass fiber reinforced heat resistance grade

● Compliance: UL

● Material characteristics: good appearance, frost free, dimensional stability, good mechanical properties, chemical coupling

● Material use: home appliance parts, structural parts, injection molding applications

● Additive: flame retardant

Inquiry Add to cart

Parameter

Material Technical Datasheet
PP FRG2 K02
FEATURES		APPLICATIONS
Good surface		Electronic and electrical applications
Dimensional stability		Home appliance components
Good mechanical performance		Internal structure of OA equipment
Chemical coupling		Structural components
Properties	Test Standard	Test Condition	Units	Typical Values
Physical Properties
Specific Gravity	ISO 1183	23℃	g/cm³	1.25
Shrinkage Rate	ISO 2577		%	0.6
Ash Content	ISO 3451		%	10
Hardness
Mechanical Properties	Test Standard	Test Condition	Units	Data
Rockwell hardness R scale	ISO 2039			105
Mechanical Properties
Mechanical Properties	Test Standard	Test Condition	Units	Data
Tensile Strength	ISO 527	10mm/min	Mpa	45
Elongation at Break	ISO 527	10mm/min	%	4
Flexural Strength	ISO 178	2.0mm/min	Mpa	70
Flexural Modulus	ISO 178	2.0mm/min	Mpa	3000
Cantilever notch impact	ISO 180	23°C	J/m2	8
Thermal Properties
Thermal Properties	Test Standard	Test Condition	Units	Data
H.D.T	ISO 75	0.45MPa	℃	140
H.D.T	ISO 75	1.8MPa	℃	130
Electrical Performance
Electrical Performance	Test Standard	Data	Units
Bulk resistance	IEC 60093	1E16	Ω
Flame Retardancy
Flame Retardancy	Test Standard	Data
Fire Rating Natural Color 0.8mm	UL94	V-0
Fire Rating Black Color 0.8mm	UL94	V-1
Fire Rating Natura/black Color 3.2mm	UL94	V-0
UL
Flame Retardancy	Test Standard	Data	Units
Fire Rating Natural Color 0.8mm	UL94	V-0
Fire Rating Black Color 0.8mm	UL94	V-1
Fire Rating Natura/black Color 3.2mm	UL94	V-0
RTI Elec Natural Color 0.8mm	UL 746B	65	°C
RTI Elec Black Color 0.8mm	UL 746B	65	°C
RTI Elec Natura/black Color 3.2mm	UL 746B	65	°C
RTI Imp Natural Color 1.6mm	UL 746B	65	°C
RTI Imp Black Color 3.0mm	UL 746B	65	°C
RTI Imp Natura/black Color 3.2mm	UL 746B	65	°C
RTI Str Natural Color 1.6mm	UL 746B	65	°C
RTI Str Black Color 3.0mm	UL 746B	65	°C
RTI Str Natura/black Color 3.2mm	UL 746B	65	°C
Injection Molding
Injection Molding			Units	Data
Drying Temperature			℃	80～90
Drying Time			h	2～4
Front Temperature			℃	180～200
Middle Temperature			℃	200～230
Temperature of The Third Section			℃	220～240
Melting temperature			℃	220~245
Maximum melting temperature			℃	260
Mold Temperature			℃	30～60
Injection speed			Medium and High speed

All Categories

V-1 V-0 Flame retardant grade 10% glass fiber reinforced pp plastic granules

Parameter

Recommended products

HB Flame retardant grade 10% glass fiber reinforced PP material

HB Flame retardant grade 20% long glass fiber reinforced pp resin price

HB Flame retardant grade 40% glass fiber reinforced pp plastic granules

HB Flame retardant grade/ 50% glass fiber reinforced pp pellets

Leave us a message

Hot categories

subscribe