● Material shape: granular
● Processing method: injection molding
● Flame retardant grade :HB
● Material properties: 50% glass fiber reinforced
● Compliance: UL
● Material characteristics: Good mechanical properties, chemical coupling, detergent resistance
● Material use: home appliance parts, structural parts, injection molding applications
| Material Technical Datasheet | ||||
| PP GF50 K01 | ||||
| FEATURES | APPLICATIONS | |||
| Chemical coupling | Electronic and electrical applications | |||
| Detergent resistant | Structural components | |||
| Good mechanical performance | Injection molding applications | |||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Specific Gravity | ISO 1183 | 23℃ | g/cm³ | 1.34 |
| Shrinkage Rate | Flow | ISO 294 | % | 0.2 |
| Shrinkage rate | Perpendicular | ISO 294 | % | 0.7 |
| Hardness | ||||
| Mechanical Properties | Test Standard | Test Condition | Units | Data |
| Rockwell hardness R scale | ISO 2039 | 112 | ||
| Mechanical Properties | ||||
| Mechanical Properties | Test Standard | Test Condition | Units | Data |
| Tensile Strength | ISO 527 | 1.0mm/min | Mpa | 11000 |
| Elongation at Break | ISO 527 | 10mm/min | % | 115 |
| Flexural Strength | ISO 178 | 2.0mm/min | Mpa | 175 |
| Flexural Modulus | ISO 178 | 2.0mm/min | Mpa | 10000 |
| Cantilever notch impact | ISO 180 | 23 ° C A-notch | KJ/m2 | 11 |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| H.D.T | ISO 75 | 0.45MPa | ℃ | 160 |
| H.D.T | ISO 75 | 1.8MPa | ℃ | 150 |
| Electrical Performance | ||||
| Electrical Performance | Test Standard | Data | Units | |
| Bulk resistance | IEC 60093 | 1E16 | Ω | |
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Fire Rating Full Color 1.6mm | UL94 | HB | ||
| Fire Rating Full Color 3.0mm | UL94 | HB | ||
| UL | ||||
| Flame Retardancy | Test Standard | Data | Units | |
| Fire Rating Full Color 1.6mm | UL94 | HB | ||
| Fire Rating Full Color 3.0mm | UL94 | HB | ||
| RTI Elec Full Color 1.6mm | UL 746B | 65 | °C | |
| RTI Elec Full Color 3.0mm | UL 746B | 65 | °C | |
| RTI Imp Full Color 1.6mm | UL 746B | 65 | °C | |
| RTI Imp Full Color 3.0mm | UL 746B | 65 | °C | |
| RTI Str Full Color 1.6mm | UL 746B | 65 | °C | |
| RTI Str Full Color 3.0mm | UL 746B | 65 | °C | |
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 80～90 | ||
| Drying Time | h | 2～4 | ||
| Front Temperature | ℃ | 180～200 | ||
| Middle Temperature | ℃ | 200～230 | ||
| Temperature of The Third Section | ℃ | 220～240 | ||
| Melting temperature | ℃ | 220~245 | ||
| Maximum melting temperature | ℃ | 260 | ||
| Mold Temperature | ℃ | 30～60 | ||
| Injection speed | Medium and high speed | |||
HB Flame retardant grade/ 10% glass fiber reinforced
Learn More
V-1 V-0 Flame retardant grade/ 10% glass fiber reinforced
Learn More
V-0 Flame retardant grade/ 10% glass fiber reinforced
Learn More
V-0 Flame retardant grade/ 20% glass fiber reinforced
Learn More
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ