● Material shape: granular
● Processing method: injection molding
● Flame retardant grade: HB
● Material properties: 30% glass fiber reinforced high heat resistance grade
● Compliance: UL
● Material characteristics: dimensional stability, low warpage, high temperature resistance
● Material use: automotive applications, spool, connector, electronic and electrical applications, electronic and electrical enclosures
| Material Technical Datasheet | ||||
| PBT G6 K01 | ||||
| PROPERTY | ||||
| 30% glass fiber reinforced high heat resistance grade | ||||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Specific Gravity | ISO 1183 | 23℃ | g/cm³ | 1.53 |
| Shrinkage Rate Flow | ISO 2577 | 23℃ | % | 0.3 |
| Shrinkage Rate Vertical | ISO 2577 | 23℃ | % | 0.9 |
| Water Absorption Rate 23 ℃ 50RH equilibrium | ISO 62 | 23 ℃ | % | 0.06 |
| Ash Content | ISO 3451 | 23℃ | % | 30 |
| Hardness | ||||
| Mechanical Properties | Test Standard | Test Condition | Units | Data |
| Rockwell hardness R scale | ISO 2039 | 120 | ||
| Mechanical Properties | ||||
| Mechanical Properties | Test Standard | Test Condition | Units | Data |
| Tensile Strength 23°C | ISO 527 | 10mm/min | Mpa | 125 |
| Elongation at Break 23°C | ISO 527 | 10mm/min | % | 2.8 |
| Flexural Strength 23°C | ISO 178 | 2.0mm/min | Mpa | 190 |
| Flexural Modulus 23°C | ISO 178 | 2.0mm/min | Mpa | 8400 |
| Cantilever notch impact 23°C | ISO 180 | 23 ° C A-notch | kJ/m² | 11 |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| H.D.T | ISO 75 | 0.45MPa | ℃ | 220 |
| H.D.T | ISO 75 | 1.8MPa | ℃ | 210 |
| Electrical Performance | ||||
| Electrical Performance | Test Standard | Data | Units | |
| Volume resistance | IEC 60093 | 1E16 | Ω.cm | |
| Insulation strength 2.0mm in oil | IEC 60243 | 23 | KV/mm | |
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Fire Rating Full Color 1.5~1.65mm | UL94 | HB | ||
| UL | ||||
| Flame Retardancy | Test Standard | Data | Units | |
| Fire Rating Full Color 1.5~1.65mm | UL94 | HB | ||
| RTI Elec Full color 1.5~1.65mm | UL 746B | 75 | °C | |
| RTI Imp Full color 1.5~1.65mm | UL 746B | 75 | °C | |
| RTI Str Full color 1.5~1.65mm | UL 746B | 75 | °C | |
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 120~140 | ||
| Drying Time | hr | 4~6 | ||
| Front Temperature | ℃ | 220~240 | ||
| Middle Temperature | ℃ | 230~250 | ||
| Temperature of The Third Section | ℃ | 240~260 | ||
| Melting temperature | ℃ | 235~255 | ||
| Maximum melting temperature | ℃ | 270 | ||
| Mold Temperature | ℃ | 40~120 | ||
| Injection speed | Medium to high speed | |||
HB Flame retardant grade/ 15% glass fiber reinforced
Learn More
Flame retardant grade: V-0 Material properties: flame retardant
Learn More
V-0 Flame retardant grade/ 15% glass fiber reinforced flame retardant high heat resistance grade
Learn More
V-0 Flame retardant grade/ 30% glass fiber reinforced
Learn More
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ