● Color: Black
● Material shape: granular
● Processing method: injection molding
● Flame retardant grade: HB
●。Material properties: 60% glass fiber reinforced high heat resistance grade
● Compliance: UL
● Material characteristics: dimensional stability, high temperature resistance, high strength and high rigidity
● Material use: automotive parts injection molding applications
| Material Technical Datasheet | ||||
| PA66 G60 K0HT | ||||
| Material Properties | ||||
| 60% glass fiber reinforced high heat resistance grade | ||||
| FEATURES | APPLICATIONS | |||
| Dimensional stability | Automotive Components | |||
| Good appearance | Injection Molding Applications | |||
| High strength | ||||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Specific Gravity | ISO 1183 | 23℃ | g/cm³ | 1.72 |
| Shrinkage Rate | ISO 2577 | Flow | % | 0.2 |
| Shrinkage Rate | ISO 2577 | Perpendicular | % | 0.5 |
| Water absorption rate | ISO 62 | 23°C 50RH balance | % | 0.9 |
| Ash content | ISO 3451 | % | 60 | |
| Hardness | ||||
| Mechanical Properties | Test Standard | Test Condition | Units | Data |
| Rockwell hardness R scale | ISO 2039 | 122 | ||
| Mechanical Properties | ||||
| Mechanical Properties | Test Standard | Test Condition | Units | Data |
| Tensile modulus | ISO 527 | 1mm/min | Mpa | 21000 |
| Tensile strength | ISO 527 | 5mm/min | Mpa | 250 |
| Elongation fracture | ISO 527 | 5mm/min | % | 2 |
| Flexural Strength | ISO 178 | 2.0mm/min | Mpa | 390 |
| Flexural Modulus | ISO 178 | 2.0mm/min | Mpa | 19000 |
| Simple supported beam notch impact | ISO 179 | 23 ° C 1eA type | KJ/m2 | 17 |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| Thermal deformation temperature | ISO 75 | 0.45MPa | ℃ | 260 |
| Thermal deformation temperature | ISO 75 | 1.8MPa | ℃ | 250 |
| Electrical Performance | ||||
| Volume resistance | IEC 60093 | 1.51E+3 | Ω.cm | |
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Fire Rating Full Color 0.8mm | UL94 | HB | ||
| Fire Rating Full Color 1.6mm | UL94 | HB | ||
| Fire Rating Full Color 3.2mm | UL94 | HB | ||
| UL | ||||
| Flame Retardancy | Test Standard | Data | Units | |
| Fire Rating Full Color 0.8mm | UL94 | HB | ||
| Fire Rating Full Color 1.6mm | UL94 | HB | ||
| Fire Rating Full Color 3.2mm | UL94 | HB | ||
| HWI Full color 1.6mm | UL 746A | 5 | PLC | |
| HWI Full color 3.2mm | UL 746A | 4 | PLC | |
| HAI Full color 1.6mm | UL 746A | 0 | PLC | |
| HAI Full color 3.2mm | UL 746A | 0 | PLC | |
| RTI Elec Full l Color 0.8mm | UL 746B | 140 | °C | |
| RTI Elec Full l Color 1.6mm | UL 746B | 140 | °C | |
| RTI Elec Full Color 3.2mm | UL 746B | 140 | °C | |
| RTI Imp Full Color 0.8mm | UL 746B | 105 | °C | |
| RTI Imp Full Color 1.6mm | UL 746B | 105 | °C | |
| RTI Imp Full Color 3.2mm | UL 746B | 125 | °C | |
| RTI Str Full Color 0.8mm | UL 746B | 110 | °C | |
| RTI Str Full Color 1.6mm | UL 746B | 110 | °C | |
| RTI Str Full Color 3.2mm | UL 746B | 130 | °C | |
| CTI | IEC 60112 | 1 | PLC | |
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 100~130 | ||
| Drying Time | h | 4~6 | ||
| Front Temperature | ℃ | 270～285 | ||
| Middle Temperature | ℃ | 280～300 | ||
| Temperature of The Third Section | ℃ | 290～305 | ||
| Melting temperature | ℃ | 270~305 | ||
| Maximum melting temperature | ℃ | 320 | ||
| Mold Temperature | ℃ | 40～120 | ||
| Injection speed | Medium and high speed | |||
Flame retardant grade: HB/ Material properties: 15% glass fiber reinforced high heat resistance grade
Learn More
Flame retardant grade: HB / Material properties: 30% glass fiber reinforced high heat resistance grade
Learn More
Flame retardant grade: HB / Material properties: 50% glass fiber reinforced high heat resistance grade
Learn More
Flame retardant grade: HB / Material properties: 35% glass fiber reinforced hydrolysis resistant grade
Learn More
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ