● Color: Black
● Material shape: granular
● Processing method: injection molding
● Flame retardant grade: HB
● Material properties: Impact modified 10% glass fiber reinforced heat stability grade high heat resistance grade
● Compliance: UL
● Material characteristics: dimensional stability, high strength, high temperature resistance, impact improvement
● Material use: Automotive parts and injection molding applications
| Material Technical Datasheet | ||||
| PA66 G2HT K01 | ||||
| FEATURES | APPLICATIONS | |||
| Stable size | Automotive Components | |||
| Good appearance | Injection Molding Applications | |||
| High temperature resistance • High strength | ||||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Specific Gravity | ISO 1183 | 23℃ | g/cm³ | 1.13 |
| Shrinkage Rate | ISO 2577 | 23℃ | % | 1.3~1.5 |
| Water absorption rate | ISO 62 | 23°C 50RH balance | % | 2.5 |
| Hardness | ||||
| Mechanical Properties | Test Standard | Test Condition | Units | Data |
| Rockwell hardness R scale | ISO 2039 | 160 | ||
| Mechanical Properties | ||||
| Mechanical Properties | Test Standard | Test Condition | Units | Data |
| Tensile modulus | ISO 527 | 10mm/min | Mpa | 3200 |
| Tensile strength | ISO 527 | 50mm/min | % | 80 |
| Flexural Strength | ISO 178 | 2.0mm/min | Mpa | 110 |
| Flexural Modulus | ISO 178 | 2.0mm/min | Mpa | 2700 |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| H.D.T | ISO 75 | 0.45MPa | ℃ | 220 |
| H.D.T | ISO 75 | 1.8MPa | ℃ | 75 |
| Electrical Performance | ||||
| Volume resistance | IEC 60093 | 1.51E+3 | Ω.cm | |
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Fire Rating Full Color 0.75mm | UL94 | V-2 | ||
| Fire Rating Full Color 3.0mm | UL94 | V-2 | ||
| UL | ||||
| Flame Retardancy | Test Standard | Data | Units | |
| Fire Rating Full Color 0.75mm | UL94 | V-2 | ||
| Fire Rating Full Color 3.0mm | UL94 | V-2 | ||
| HWI Full color 0.75mm | UL 746A | 4 | PLC | |
| HWI Full color 3.0mm | UL 746A | 4 | PLC | |
| HAI Full color 0.75mm | UL 746A | 0 | PLC | |
| HAI Full color 3.0mm | UL 746A | 0 | PLC | |
| RTI Elec Full l Color 0.75mm | UL 746B | 65 | °C | |
| RTI Elec Full Color 3.0mm | UL 746B | 65 | °C | |
| RTI Imp Full Color 0.75mm | UL 746B | 65 | °C | |
| RTI Imp Full Color 3.0mm | UL 746B | 65 | °C | |
| RTI Str Full Color 0.75mm | UL 746B | 65 | °C | |
| RTI Str Full Color 3.0mm | UL 746B | 65 | °C | |
| CTI | IEC 60112 | 0 | PLC | |
| Insulation strength | ASTM D149 | 11 | KV/mm | |
| GWFI 1.5mm | IEC 60695-2-12 | 960 | °C | |
| GWFI 3.0mm | IEC 60695-2-12 | 960 | °C | |
| GWIT 1.5mm | IEC 60695-2-13 | 700 | °C | |
| GWIT 3.0mm | IEC 60695-2-13 | 700 | °C | |
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 100~130 | ||
| Drying Time | h | 4~6 | ||
| Front Temperature | ℃ | 270～285 | ||
| Middle Temperature | ℃ | 280～290 | ||
| Temperature of The Third Section | ℃ | 290～300 | ||
| Melting temperature | ℃ | 270~290 | ||
| Maximum melting temperature | ℃ | 320 | ||
| Mold Temperature | ℃ | 40～100 | ||
| Injection speed | Medium and high speed | |||
Flame retardant grade: HB/ Material properties: 15% glass fiber reinforced high heat resistance grade
Learn More
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ