PA6 G50 K01 50% glass fiber reinforced pa6 50gf

● Material shape: granular

● Processing method: injection molding

● Flame retardant grade: HB

● Material properties: 50% glass fiber reinforced

● Compliance: UL

● Material characteristics: good appearance, dimensional stability, good mechanical properties

● Material use: gas car parts, electronic and electrical applications, home appliance parts, electrical appliances, power tool handles, sporting goods applications, main plastic molding applications

Inquiry Add to cart

Parameter

Material Technical Datasheet
PA6 G50 K01
Material Properties
50% glass fiber reinforced
FEATURES		APPLICATIONS
Good appearance		Home appliance applications
Dimensional stability		Electric tool handle
Good mechanical performance		Sports Goods Application
		Injection molding applications
Properties	Test Standard	Test Condition	Units	Typical Values
Physical Properties
Specific Gravity	ISO 1183	23°C	g/cm³	1.55
Shrinkage Rate	ISO 2577	flow	%	0.2
Shrinkage Rate	ISO 2577	perpendicular	%	0.6
Water absorption rate	ISO 62	23 ° C 50RH balance	%	1.4
Ash content	ISO 3451		%	50
Mechanical Properties
Mechanical Properties	Test Standard	Test Condition	Units	Data
Tensile Strength	ISO 527	23 ° C 10mm/min	Mpa	205
Elongation at Break	ISO 527	23 ° C 10mm/min	%	2.2
Flexural Strength	ISO 178	23 ° C 2.0mm/min	Mpa	300
Flexural Modulus	ISO 178	23 ° C 2.0mm/min	Mpa	12500
Cantilever beam notch impact	ISO 180	23 ° C	kJ/m2	20
Thermal Properties
Thermal Properties	Test Standard	Test Condition	Units	Data
Thermal deformation temperature	ISO 75	0.45MPa	℃	220
Thermal deformation temperature	ISO 75	1.8MPa	℃	215
Electrical Performance
Electrical Performance	Test Standard	Data	Units
Volume resistance	IEC 60093	1.51E+3	Ω.cm
Flame Retardancy
Flame Retardancy	Test Standard	Data
Fire Rating Full Color 0.75mm	UL94	HB
Fire Rating Full Color 1.6mm	UL94	HB
Fire Rating Full Color 3.0mm	UL94	HB
UL
Flame Retardancy	Test Standard	Data	Units
Fire Rating Full Color 0.75mm	UL94	HB
Fire Rating Full Color 1.6mm	UL94	HB
Fire Rating Full Color 3.0mm	UL94	HB
HWI Full Color 0.75mm	UL 746A	4	PLC
HWI Full Color 1.6mm	UL 746A	2	PLC
HWI Full Color 3.0mm	UL 746A	0	PLC
HAI Full Color 0.75mm	UL 746A	0	PLC
HAI Full Color 1.6mm	UL 746A	0	PLC
HAI Full Color 3.0mm	UL 746A	0	PLC
RTI Elec Full Color 0.75mm	UL 746B	65	PLC
RTI Elec Full Color 1.6mm	UL 746B	65	°C
RTI Elec Full Color 3.0mm	UL 746B	65	°C
RTI Imp Full Color 0.75mm	UL 746B	65	°C
RTI Imp Full Color 1.6mm	UL 746B	65	°C
RTI Imp Full Color 3.0mm	UL 746B	65	°C
RTI Str Full Color 0.75mm	UL 746B	65	°C
RTI Str Full Color 1.6mm	UL 746B	65	°C
RTI Str Full Color 3.0mm	UL 746B	65	°C
Insulation strength	ASTM D149	11	KV/mm
Arc resistance	ASTM D495	5	PLC
GWFI 0.75mm	IEC 60695-2-12	700	°C
GWFI 1.6mm	IEC 60695-2-12	700	°C
GWFI 3.0mm	IEC 60695-2-12	700	°C
GWIT 0.75mm	IEC 60695-2-13	725	°C
GWIT 1.6mm	IEC 60695-2-13	725	°C
GWIT 3.0mm	IEC 60695-2-13	725	°C
CTI	IEC 60112	0	PLC
Injection Molding
Injection Molding			Units	Data
Drying Temperature			℃	90～110
Drying Time			h	4～6
Front Temperature			℃	230～250
Middle Temperature			℃	250～270
Temperature of The Third Section			℃	260～280
Melting temperature			℃	255~280
Maximum melting temperature			℃	300
Mold Temperature			℃	50～120
Injection speed			High speed

All Categories

PA6 G50 K01 50% glass fiber reinforced pa6 50gf

Parameter

Recommended products

PA6 G2 K01 10% glass fiber reinforced pa6 gf10

PA6 G3 K01 15% glass fiber reinforced pa6 gf15

PA6 G7 K01 35% glass fiber reinforced nylon pa6 material

PA6 FRG6 K2NP 30% glass fiber reinforced halogen-free flame retardant pa6 particles