PA6 G2 K01 10% glass fiber reinforced pa6 gf10

● Material shape: granular

● Processing method: injection molding

● Flame retardant grade: HB

● Material properties: 10% glass fiber reinforced

● Compliance: UL

● Material characteristics: good appearance, dimensional stability, good mechanical properties

● Material use: Home appliance application, power tool handle, sporting goods application, injection molding application

Inquiry Add to cart

Parameter

Material Technical Datasheet
PA6 G2 K01
Material Properties
10% glass fiber reinforced
FEATURES		APPLICATIONS
Good appearance		Home appliance applications
Dimensional stability		Electric tool handle
Good mechanical performance		Sports Goods Application
		Injection molding applications
Properties	Test Standard	Test Condition	Units	Typical Values
Physical Properties
Specific Gravity	ISO 1183	23°C	g/cm³	1.2
Shrinkage Rate	ISO 2577	flow	%	0.4～0.7
Shrinkage Rate	ISO 2577	perpendicular	%	4.2
Water absorption rate	ISO 62	23 ° C 50RH balance	%	25
Ash content	ISO 3451		%	10
Mechanical Properties
Mechanical Properties	Test Standard	Test Condition	Units	Data
Tensile Strength	ISO 527	23 ° C 10mm/min	Mpa	100
Elongation at Break	ISO 527	23 ° C 10mm/min	%	3.7
Flexural Strength	ISO 178	23 ° C 2.0mm/min	Mpa	145
Flexural Modulus	ISO 178	23 ° C 2.0mm/min	Mpa	4200
Cantilever beam notch impact	ISO 180	23 ° C	kJ/m2	6
Thermal Properties
Thermal Properties	Test Standard	Test Condition	Units	Data
Thermal deformation temperature	ISO 75	0.45MPa	℃	205
Thermal deformation temperature	ISO 75	1.8MPa	℃	185
Electrical Performance
Electrical Performance	Test Standard	Data	Units
Volume resistance	IEC 60093	1E14+3	Ω.cm
Flame Retardancy
Flame Retardancy	Test Standard	Data
Fire Rating Full Color 0.75mm	UL94	HB
Fire Rating Full Color 1.6mm	UL94	HB
Fire Rating Full Color 3.0mm	UL94	HB
UL
Flame Retardancy	Test Standard	Data	Units
Fire Rating Full Color 0.75mm	UL94	HB
Fire Rating Full Color 1.6mm	UL94	HB
Fire Rating Full Color 3.0mm	UL94	HB
HWI Full Color 0.75mm	UL 746A	4
HWI Full Color 1.6mm	UL 746A	2	PLC
HWI Full Color 3.0mm	UL 746A	0	PLC
HAI Full Color 0.75mm	UL 746A	0	PLC
HAI Full Color 1.6mm	UL 746A	0	PLC
HAI Full Color 3.0mm	UL 746A	0	PLC
RTI Elec Full Color 0.75mm	UL 746B	65	PLC
RTI Elec Full Color 1.6mm	UL 746B	65	°C
RTI Elec Full Color 3.0mm	UL 746B	65	°C
RTI Imp Full Color 0.75mm	UL 746B	65	°C
RTI Imp Full Color 1.6mm	UL 746B	65	°C
RTI Imp Full Color 3.0mm	UL 746B	65	°C
RTI Str Full Color 0.75mm	UL 746B	65	°C
RTI Str Full Color 1.6mm	UL 746B	65	°C
RTI Str Full Color 3.0mm	UL 746B	65	°C
GWFI 0.75mm	IEC 60695-2-12	700	°C
GWFI 1.6mm	IEC 60695-2-12	700	°C
GWFI 3.0mm	IEC 60695-2-12	700	°C
GWIT 0.75mm	IEC 60695-2-13	725	°C
GWIT 1.6mm	IEC 60695-2-13	725	°C
GWIT 3.0mm	IEC 60695-2-13	725	°C
CTI	IEC 60112	0	PLC
Injection Molding
Injection Molding			Units	Data
Drying Temperature			℃	90～110
Drying Time			h	4～6
Front Temperature			℃	230～250
Middle Temperature			℃	250～270
Temperature of The Third Section			℃	260～280
Melting temperature			℃	255~280
Maximum melting temperature			℃	300
Mold Temperature			℃	50～120
Injection speed			High speed

All Categories

PA6 G2 K01 10% glass fiber reinforced pa6 gf10

Parameter

Recommended products

PA6 G3 K01 15% glass fiber reinforced pa6 gf15

PA6 G50 K01 50% glass fiber reinforced pa6 50gf

PA6 FRG6 K01 V-0 Flame retardant grade pa6 resin

PA6 G8HT K01 40% glass fiber reinforced heat stability grade nylon pa6