HB Flame retardant grade high temperature resistance and high rigidity pp plastic particles

● Color: natural

● Material shape: granular

● Processing method: injection molding

● Flame retardant grade: HB

● Compliance: UL

● Material characteristics: high temperature resistance and high rigidity

● Material use: appliance parts, automotive applications, household goods

Inquiry Add to cart

Parameter

Material Technical Datasheet
PP FR K05
FEATURES		APPLICATIONS
High rigidity		Electronic and electrical applications
		Home Furnishings
		Injection Molding Applications
Properties	Test Standard	Test Condition	Units	Typical Values
Physical Properties
Specific Gravity	ISO 1183	23℃	g/cm³	1.31
Shrinkage Rate	ISO 2577		%	1.0~1.3
Melt index	ISO 1133	220°C 2.16kg	%	5
Hardness
Mechanical Properties	Test Standard	Test Condition	Units	Data
Rockwell hardness R scale	ASTM D785			85
Mechanical Properties
Mechanical Properties	Test Standard	Test Condition	Units	Data
Tensile Strength	ISO 527	50mm/min	Mpa	28
Elongation at Break	ISO 527	50mm/min	%	30
Flexural Strength	ISO 178	2.0mm/min	Mpa	42
Flexural Modulus	ISO 178	2.0mm/min	Mpa	2700
Cantilever notch impact	ISO 180	23°C 4.0mm	J/m2	4.5
Thermal Properties
Thermal Properties	Test Standard	Test Condition	Units	Data
H.D.T	ISO 75	1.8MPa 4.0mm	℃	120
Electrical Performance
Electrical Performance	Test Standard	Data	Units
CTI 3.0mm solution A	IEC 60112	600	V
Flame Retardancy
Flame Retardancy	Test Standard	Data
Fire Rating Full color 0.8mm	UL94	V-0
Fire Rating Full color 1.5mm	UL94	V-0
Fire Rating Full color 2.0mm	UL94	V-0 5VA
Fire Rating Full color 3.2mm	UL94	V-0 5VA
Glowing wire relative temperature	IEC 60695	960℃
UL
Flame Retardancy	Test Standard	Data	Units
Fire Rating Full color 0.8mm	UL94	V-0
Fire Rating Full color 1.5mm	UL94	V-0
Fire Rating Full color 2.0mm	UL94	V-0 5VA
Fire Rating Full color 3.0mm	UL94	V-0 5VA
HWI Full color 0.8mm	UL 746A	4	PLC
HWI Full color 1.5mm	UL 746A	2	PLC
HWI Full color 2.0mm	UL 746A	2	PLC
HWI Full color 3.0mm	UL 746A	2	PLC
HAI Full color 0.8mm	UL 746A	0	PLC
HAI Full color 1.5mm	UL 746A	0	PLC
HAI Full color 2.0mm	UL 746A	0	PLC
HAI Full color 3.0mm	UL 746A	0	PLC
RTI Elec Full color 0.8mm	UL 746B	125	°C
RTI Elec Full color 1.5mm	UL 746B	125	°C
RTI Elec Full color 2.0mm	UL 746B	125	°C
RTI Elec Full color 3.0mm	UL 746B	125	°C
RTI Imp Full color 0.8mm	UL 746B	120	°C
RTI Imp Full color 1.5mm	UL 746B	120	°C
RTI Imp Full color 2.0mm	UL 746B	120	°C
RTI Imp Full color 3.0mm	UL 746B	120	°C
RTI Str Full color 0.8mm	UL 746B	120	°C
RTI Str Full color 1.5mm	UL 746B	120	°C
RTI Str Full color 2.0mm	UL 746B	120	°C
RTI Str Full color 3.0mm	UL 746B	120	°C
CTI	IEC 60112	0	PLC
Insulation strength	ASTM D149	34	KV/mm
Injection Molding
Injection Molding			Units	Data
Drying Temperature			℃	90～100
Drying Time			h	2
Front Temperature			℃	180～200
Middle Temperature			℃	190～210
Temperature of The Third Section			℃	190～210
Melting temperature			℃	200~230
Maximum melting temperature			℃	250
Mold Temperature			℃	30～60
Injection speed			Medium speed

All Categories

HB Flame retardant grade high temperature resistance and high rigidity pp plastic particles

Parameter

Recommended products

Flame retardant grade :V-1 V-0 pp powder polypropylene

V-0 Flame retardant grade pp material polypropylene

V-0 Flame retardant grade flame retardant pp homopolymer grade plastic

V-0 5VA Flame retardant grade halogen-free flame retardant pp granules polypropylene

Leave us a message

Hot categories

subscribe