● Color: Color is optional
● Material shape: granular
● Processing method: extrusion molding
● Flame retardant grade :V-0
● Material properties: flame retardant
● Material characteristics: high rigidity
● Material use: pipe profile extrusion molding application
● Additive: flame retardant
| Material Technical Datasheet | ||||
| ABS FRHF K0EX | ||||
| Material Properties | ||||
| Flame retardant | ||||
| FEATURES | APPLICATIONS | |||
| Pipe | ||||
| High rigidity | Profile | |||
| Extrusion molding applications | ||||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Specific Gravity | ISO 1183 | 23℃ | g/cm³ | 1.21 |
| Shrinkage rate | ISO 294 | 23℃ | % | 0.4～0.7 |
| Melt index | ISO 1133 | 200°C 5kg | g/10min | 2.5 |
| Melt index | ISO 1133 | 220°C 10kg | g/10min | 20 |
| Hardness | ||||
| Mechanical Properties | Test Standard | Test Condition | Units | Data |
| Rockwell hardness R scale | ISO 2039 | 104 | ||
| Mechanical Properties | ||||
| Mechanical Properties | Test Standard | Test Condition | Units | Data |
| Tensile Strength | ASTM D638 | 50mm/min | Mpa | 38 |
| Elongation at Break | ASTM D638 | 50mm/min | % | 10 |
| Flexural Strength | ASTM D790 | 2.0mm/min | Mpa | 60 |
| Flexural Modulus | ASTM D790 | 2.0mm/min | Mpa | 2300 |
| Impact Strength, Notched | ASTM D256 | 23 ° C 4.0mm A-notch | kJ/m2 | 15 |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| Thermal deformation temperature | ISO 75 | 0.45MPa 4.0mm | ℃ | 83 |
| Thermal deformation temperature | ISO 75 | 1.8MPa 4.0mm | ℃ | 74 |
| Vicat softening temperature | ISO 306 | 120°C/hr 10N | ℃ | 93 |
| Vicat softening temperature | ISO 306 | 50°C/hr 50N | ℃ | 84 |
| Electrical Performance | ||||
| Electrical Performance | Test Standard | Data | Units | |
| Volume resistance | ASTM D257 | 1E14 | Ω.com | |
| Insulation Strength 1.6mm | ASTM D149 | 22 | KV/mm | |
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Fire Rating | UL94 | V-0 | ||
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 70～80 | ||
| Drying Time | h | 3～5 | ||
| Front Temperature | ℃ | 150～170 | ||
| Middle Temperature | ℃ | 160～180 | ||
| Temperature of The Third Section | ℃ | 170～190 | ||
| Melting temperature | ℃ | 160～185 | ||
| Maximum melting temperature | ℃ | 200 | ||
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ