Home > Product > Raw Material > ABS
| Material Technical Datasheet | ||||
| ABS AF342 | ||||
| FEATURES | APPLICATIONS | |||
| Flame Retardant | ||||
| Properties | Test Standard | Test Condition | Units | Typical Values |
| Physical Properties | ||||
| Density | ASTM D792 | 23℃ | g/10cm³ | 1.19 |
| shrinkage Flow | ASTM D955 | 23℃,3.2mm | % | 0.4 |
| shrinkage xFlow | ASTM D955 | 23℃,3.2mm | % | 0.7 |
| melt index | ASTM D1238 | 220℃,10KG | g/10min | 37 |
| hardness | ||||
| Rockwell hardness | ASTM D785 | R(Scale） | 103 | |
| Mechanical Properties | ||||
| Mechanical Properties | Test Standard | Test Condition | Units | Data |
| Tensile Modulus | ASTM D638 | 50 mm/min, 23℃ | Mpa | 2160 |
| Tensile Strength | ASTM D638 | 50 mm/min, 23℃ | Mpa | 44.1 |
| Elongation at yield | ASTM D638 | 50 mm/min, 23℃ | % | 5 |
| Elongation at Break | ASTM D638 | 50 mm/min, 23℃ | % | 20 |
| Flexural Strength | ASTM D790 | 15 mm/min, 23℃ | Mpa | 68.6 |
| Flexural Modulus | ASTM D790 | 15mm/min, 23℃ | Mpa | 2350 |
| Izod Notched Impact | ASTM D256 | 23°C 3.2mm | J/m | 206 |
| Izod Notched Impact | ASTM D256 | -30°C 3.2mm | J/m | 177 |
| Izod Notched Impact | ASTM D256 | 23°C 6.4mm | J/m | 58.8 |
| Izod Notched Impact | ASTM D256 | -30°C 6.4mm | J/m | 58.8 |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| H.D.T Unannealed 0.45Mpa | ASTM D648 | 0.45MPa 6.4mm | ℃ | 89 |
| H.D.T Unannealed 1.8Mpa | ASTM D648 | 1.8MPa 6.4mm | ℃ | 81 |
| Vicat Softening Temperature | ASTM D1525 | 50℃/hr 50N | ℃ | 88 |
| Electrical properties | ||||
| Volume resistance | ASTM D257 | Ω.cm | 1.00E+12 | |
| Dielectric Srength | ASTM D149 | KV/mm | 36 | |
| Arc resistance | ASTM D495 | s | 3 | |
| CTI | V | 500 | ||
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Fire Rating all Color 1.5mm | UL94 | v-0 | ||
| Fire Rating all Color 2.0mm | UL94 | v-0.5VB | ||
| Fire Rating all Color 2.5mm | UL94 | v-0.5VB | ||
| Fire Rating all Color 3.0mm | UL94 | v-0.5VB | ||
| Fire Rating GY 3.0mm | UL94 | V-0 RP35 | ||
| UL | ||||
| Flame Retardancy | Test Standard | Data | Units | |
| UL FlamingRating all Color 1.5mm | UL94 | v-0 | ||
| HWI ALL 1.5mm | UL746A | 4 | PLC | |
| HAI ALL 1.5mm | UL746A | 0 | PLC | |
| RTI Elec all 1.5mm | UL746B | 60 | ℃ | |
| RTI lmp all 1.5mm | UL746B | 60 | ℃ | |
| RTI str all 1.5mm | UL746B | 60 | ℃ | |
| UL FlamingRating all Color 2.0mm | UL 94 | v-0.5VB | ||
| HWI ALL2.0mm | UL 746A | 4 | PLC | |
| HAI ALL2.0mm | UL 746A | 0 | PLC | |
| RTI Elec all 2.0mm | UL 746B | 60 | ℃ | |
| RTI lmp all 2.0mm | UL 746B | 60 | ℃ | |
| RTI str all 2.0mm | UL 746B | 60 | ℃ | |
| UL FlamingRating all Color 2.5mm | UL94 | v-0.5vB | ||
| HWI ALL 2.5mm | UL746A | 4 | PLC | |
| HAI ALL 2.5mm | UL746A | 0 | PLC | |
| RTI Elec all2.5mm | UL746B | 60 | ℃ | |
| RTI lmp all 2.5mm | UL746B | 60 | ℃ | |
| RTI str all 2.5mm | UL746B | 60 | ℃ | |
| UL FlamingRating all Color 3.0mm | UL 94 | v-0.5vB | ||
| HWI ALL3.0mm | UL 746A | 4 | PLC | |
| HAI ALL3.0mm | UL 746A | 0 | PLC | |
| RTI Elec all 3.0mm | UL 746B | 60 | ℃ | |
| RTI lmp all 3.0mm | UL 746B | 60 | ℃ | |
| RTI str all 3.0mm | UL 746B | 60 | ℃ | |
| UL FlamingRating GY 3.0mm | UL 94 | v-0 RP35 | ||
| HWI GY 3.0mm | UL 746A | 1 | PLC | |
| HAI GY 3.0mm | UL 746A | 0 | PLC | |
| RTI Elec GY 3.0mm | UL 746B | 60 | ℃ | |
| RTI lmp GY 3.0mm | UL 746B | 60 | ℃ | |
| RTI str GY 3.0mm | UL 746B | 60 | ℃ | |
| CTI | IEC 60112 | 1 | PLC | |
| Dielectric strength | ASTM D149 | 36 | KV/mm | |
| Volume resistance | ASTM D257 | 1.0E12 | Ω.cm | |
| HVTR | UL 746A | 4 | PLC | |
| Dielectric stability | UL 746 | 0 | % | |
| Arc resistance | ASTM D495 | 7 | PLC | |
Copyright © Shanghai Qishen Plastic Industry Co.,ltd. All Rights Reserved.
EN
AR
CS
NL
FI
FR
DE
HI
IT
JA
KO
PL
PT
RU
ES
TL
ID
VI
ET
GL
HU
TH
TR
BE
AZ
BN
BS
LA
UZ